Single Margin Zn-Al MPET Film With Ramp Resistance

The 1.9um-12um polyester plain film serves as the foundation for MPET films. 620mm is the typical width.

A coating machine uses a high vacuum to melt, evaporate, and deposit high-purity zinc and aluminum on the base film. After an incredibly thin metal layer has been created, a metalized polypropylene film is created on the surface.

After the partial breakdown of the film dielectric, the metalized film has a self-healing function that causes it to naturally revert to the electrical performance phenomenon before the breakdown. The metalized film is covered on one or both sides of the edge or in the center to create a blank insulating strip without evaporating metal, known as the margin, and its width is referred to as the margin in the actual fabrication of capacitors.


Specification of Single Margin Zn-Al MPET Film With Ramp Resistance


Base film

Polyester film

Normal thickness

1.9μm ~12.0μm

Margin type

Single

Coating metal

Zinc-Aluminum alloy

Coating side

Single

Edge structure

Heavy edge


Square resistance: Normal film Width and Margin


Reinforced resistance

Normal resistance

(2~4)Ω/ohms

(6~25)Ω/ohms ramp

(2~4)Ω/ohms

(6~20)Ω/ohms ramp

(2~4)Ω/ohms

(6~30)Ω/ohms ramp

(1~3)Ω/ohms

(4~26)Ω/ohms ramp



Width(mm)

Margin(mm)

Width(mm)

Margin(mm)

45

2.5

70

2.5

50

2.0/2.5

75

2.0/2.5

55

2.0/2.5

80

2.0/2.5

60

2.0/2.5

85

2.0/2.5

62.5

4

100

2.0/2.5

65

2.5

125

2.0

Note: If a customer needs other resistance, film width, or margin, please contact us.


Inside/outside core diameter:


Inside core diameter/Tolerance

Outside core diameter/Tolerance

75mm

+1/-0.5mm

220

280

320

±20mm

±20mm

±20mm

Note: A pair tolerance of outside core diameter ≤2mm.


Specifications of the metalized polyester film:


Properties

Unit

Typical value

Density

g/cm3

1.4

Thickness

µm

<5

5~12

≥12

Tensile Strength

MD (MPa)

≥84

≥108

≥120

Elongation at Break

MD (%)

≥22

≥33

≥44

Elastic Modulus

MD (MPa)

3500

Break-down Voltage

V/µm

≥200

( 23°C, DC )

≥250

( 23°C, DC )

Heat Shrinkage

MD (%)

≤2.5 ( 150°C, 10min)

Surface Roughness

µm

0.095

Melting Point

256

Volume Resistivity

Ω.m

>1015

( 23°C, Humidity 50%)

Dielectric Constant


3.2

(20℃,1KHz)

Dissipation Factor

-

≤60×10-4

(20℃,1KHz )

RC

ΩF

≥1×104


Packing of Single Margin Zn-Al MPET Film With Ramp Resistance

  • Film rolls are packed in plastic bags, vacuumed and put into desiccant for heat sealing.

  • The Bags are marked with type labels, mark thickness width, free margin width and resistance.

  • The bags are packed in carton cases.

  • The cartons are wrapped by wooden cases or reinforced carton.

Packing of Single Margin Zn-Al  MPET Film With Ramp Resistance

Products

Contact us
Add:
No.1771 Qifeng Road, Tongling City, Anhui Province, China

We've got the high-quality capacitors, contact us now!